A highly porous (~90%) interconnected hydroxyapatite/wollastonite (HA/WS) scaffolds were prepared by polymeric sponge replica method using a slurry containing HA:Calcium silicate in the weight ratio of 50:50 and sintered at 1300 oC. The phase purity of the scaffolds were analyzed by using XRD. The pore size, pore structure, microstructure and elemental analysis of the scaffolds before and after SBF soaking were analyzed using SEM and EDS. In-vitro bioactivity and bioresorbability confirmed the feasibility of the developed scaffolds. The HA/WS scaffold shows two fold increase in the compressive strength compared to pure HA scaffold.

Autore Pugliese

• Licciulli Antonio Alessandro , Sannino Alessandro , Scalera Francesca , Gervaso Francesca

Tutti gli autori

• Kunjalukkal Padmanabhan S. , Carrozzo M. , Gervaso F. , Scalera F. , Sannino A. , Licciulli A.

Titolo volume/Rivista

Non Disponibile

Anno di pubblicazione

2012

ISSN

Non Disponibile

ISBN

Non Disponibile

Numero di citazioni Wos

Nessuna citazione

Ultimo Aggiornamento Citazioni

Non Disponibile

Numero di citazioni Scopus

Non Disponibile

0

Ultimo Aggiornamento Citazioni

28/04/2018

Settori ERC

Non Disponibile

Codici ASJC

Non Disponibile