Abstract

ZnO nanocrystals (2.5-4.5 nm) were prepared by a wet chemical method based on alkaline-activated hydrolysis and condensation of zinc acetate solutions. Dropcasting of the nanocrystals onto alumina substrates allowed the fabrication of gas sensing devices, that were tested towards NO2, acetone and methanol and showed promising results. At low working temperature, the ZnO quantum dots based sensors are selective to nitrogen oxide, in fact a good sensitivity is shown at 200 degrees C at low concentration (2 ppm), while at temperature above 350 degrees C, high responses are obtained for acetone and methanol. The results obtained are stimulating for further developing of nano-ZnO based sensor devices.

Autore Pugliese

• Forleo Angiola , Francioso Luca Nunzio , Siciliano Pietro Aleardo , Capone Simonetta

Tutti gli autori

• Forleo A.; Francioso L.; Capone S.; Siciliano P.; Lommens P.; Hens Z.

Titolo volume/Rivista

Sensors and actuators. B, Chemical

Anno di pubblicazione

2010

ISSN

0925-4005

ISBN

Non Disponibile

Numero di citazioni Wos

Nessuna citazione

Ultimo Aggiornamento Citazioni

Non Disponibile

Numero di citazioni Scopus

Non Disponibile

Ultimo Aggiornamento Citazioni

Non Disponibile

Settori ERC

Non Disponibile

Codici ASJC

Non Disponibile