Abstract

High performance electrocatalytic hydrocarbon thin films containing Pt nano-clusters are deposited bysimultaneous plasma polymerization of ethylene and sputtering of a Pt target. The proposed syntheticapproach largely simplifies the PEMFC electrocatalyst fabrication process with respect to conventionalmethods. The deposition of the hydrocarbon matrix provides the mechanical support and electroniccontinuity, ensuring a uniform metal dispersion, avoiding Pt nanoparticle agglomeration. The Ptcatalyst is dispersed as small vertically stacked clusters with size less than 10 nm in columnar thin(250-500 nm) films. PEMFC testing with plasma deposited 500 nm thick film and 0.513 mg cm2 Pt loadas anodic electrocatalyst led to a maximum reproducible power density as high as 300 mW cm2.

Autore Pugliese

• Palumbo Fabio

Tutti gli autori

• E. Dilonardo; A. Milella; F. Palumbo; R. D'Agostino; F. Fracassi; J. Thery; S. Martin; G. Barucca; P. Mengucci

Titolo volume/Rivista

Journal of materials chemistry

Anno di pubblicazione

2010

ISSN

0959-9428

ISBN

Non Disponibile

Numero di citazioni Wos

Nessuna citazione

Ultimo Aggiornamento Citazioni

Non Disponibile

Numero di citazioni Scopus

Non Disponibile

Ultimo Aggiornamento Citazioni

Non Disponibile

Settori ERC

Non Disponibile

Codici ASJC

Non Disponibile