Nanostructure of buried interface layers in TiO(2) anatase thin films grown on LaAlO(3) and SrTiO(3) substrates

Torna indietro

Abstract

TiO2 anatase thin films grown by pulsed laser deposition are investigated by high resolution transmission electron microscopy and high angle annular dark field scanning transmission electron microscopy. The analyses provide evidence of a peculiar growth mode of anatase on LaAlO3 and SrTiO3 characterized by the formation of an epitaxial layer at the film/substrate interface, due to cationic diffusion from the substrate into the film region. Pure TiO2 anatase growth occurs in both specimens above a critical thickness of about 20 nm. The microstructural and chemical characterization of the samples is presented and discussed in the framework of oxide interface engineering.

Autore Pugliese

Tutti gli autori

  • Ciancio R.; Carlino E.; Aruta C.; Maccariello D.; Miletto Granozio F.; Scotti di Uccio U.

Titolo volume/Rivista

Nanoscale

Anno di pubblicazione

2012

ISSN

2040-3364

ISBN

Non Disponibile

Numero di citazioni Wos

Nessuna citazione

Ultimo Aggiornamento Citazioni

Non Disponibile

Numero di citazioni Scopus

Non Disponibile

Ultimo Aggiornamento Citazioni

Non Disponibile

Settori ERC

Non Disponibile

Codici ASJC

Non Disponibile