Abstract

High densities of self-catalyzed Si nanowires have been grown at temperatures down to 320 degrees C on different Si substrates, whose surfaces have been roughened by simple physical or chemical treatments. The particular substrates are Si(110) cleavage planes, chemically etched Si(111) surfaces and microcrystalline Si obtained by laser annealing thin amorphous Si layers. The NW morphology depends on the growth surface. Transmission electron microscopy indicates that the NWs are made of pure Si with a crystalline core structure. Reflectivity measurements confirm this latter finding.

Autore Pugliese

• Cuscuna' Massimo

Tutti gli autori

• Cuscunà M.; Convertino A.; Mariucci L.; Fortunato G.; Felisari L.; Nicotra G.; Spinella C.; Pecora A.; Martelli F.

Titolo volume/Rivista

Nanotechnology

Anno di pubblicazione

2010

ISSN

0957-4484

ISBN

Non Disponibile

Numero di citazioni Wos

Nessuna citazione

Ultimo Aggiornamento Citazioni

Non Disponibile

Numero di citazioni Scopus

Non Disponibile

Ultimo Aggiornamento Citazioni

Non Disponibile

Settori ERC

Non Disponibile

Codici ASJC

Non Disponibile