Polycrystalline diamond films with a thickness of about 2 μm were deposited by chemical vapour deposition on silicon substrates in continuous and pulsed wave regimes with duty cycle between 25% and 100%. The thermoluminescent behaviour of these films was analysed in the temperature range 323–723 K after β irradiation with doses in the range 7–107 Gy. All the films exhibit a dosimetric peak centred at about 592 K, showing a good linearity in the whole investigated dose range. The thermoluminescence analyses show that the intensity of the dosimetric peak is maximum for the continuous wave film, while it decreases for the pulsed wave samples. The variation of the crystalline quality and the purity of the films with the employed duty cycle, investigated via micro-Raman spectroscopy and room-temperature photoluminescence, indicates that the continuous wave (duty cycle=100%) film has the best quality, corresponding to the highest thermoluminescence efficiency.

Autore Pugliese

• Schiavulli Luigi

Tutti gli autori

• SCHIAVULLI L.

Titolo volume/Rivista

Non Disponibile

Anno di pubblicazione

2010

ISSN

0925-9635

ISBN

Non Disponibile

Numero di citazioni Wos

Nessuna citazione

Ultimo Aggiornamento Citazioni

Non Disponibile

Numero di citazioni Scopus

5

Ultimo Aggiornamento Citazioni

Non Disponibile

Settori ERC

Non Disponibile

Codici ASJC

Non Disponibile