Synthesis of β-Ga2O3 microstructures with efficient photocatalytic activity by annealing of GaSe single crystal

Torna indietro

Abstract

The synthesis of new β-Ga2O3 microstructures was achieved through rapid annealing of GaSe single crystal at 850 °C in oxygen-ammonia co-flow for 30-120 min duration. The obtained micro-flowers and micro-leaves were carefully characterized through X-ray diffraction, scanning electron microscopy and Raman spectroscopy. SEM images demonstrated that the product consisted of flower-shaped microstructures, which as time elapsed evolved into leaves-like dendritic microstructures. These microstructures started off directly from oxidized single crystal. A possible growth mechanism was also proposed. Experimental results evidenced that synthesized microstructures exhibited good photocatalytic activity, better than commercial TiO2 powder (Degussa P25).

Autore Pugliese

Tutti gli autori

  • Filippo E. , Tepore M. , Baldassarre F. , Siciliano T. , Micocci G. , Quarta G. , Calcagnile L. , Tepore A.

Titolo volume/Rivista

APPLIED SURFACE SCIENCE

Anno di pubblicazione

2015

ISSN

0169-4332

ISBN

Non Disponibile

Numero di citazioni Wos

Nessuna citazione

Ultimo Aggiornamento Citazioni

Non Disponibile

Numero di citazioni Scopus

2

Ultimo Aggiornamento Citazioni

28/04/2018

Settori ERC

Non Disponibile

Codici ASJC

Non Disponibile