We investigated by means of transmission electron microscopy (TEM) GaAs-AlGaAs core-shell nanowires (NWs) grown by Au-catalyzed metalorganic vapor phase epitaxy under As-rich vapor conditions. The structural analysis reveals that the NWs exhibit zincblende phase only and a very low density of twin defects along the NW trunk; a higher amount of twins around the NW axial (growth) direction occur instead within a tapered region closeby the NW tip. We correlate this finding to the Alrich composition of the tapered region, as deduced by scanning-TEM (STEM) mass contrast analysis, this region being the effect of residual Au-assisted self-assembly of the material during shell overgrowth. In addition a few percent of NWs show branching during their growth, and we determine the crystal properties and defects of branched NWs. We propose that this phenomenon may be induced by Au nanoparticle instabilities during NW growth and further demonstrate that twin defects occur at the NW branching points.

Autore Pugliese

• Lovergine Nicola

Tutti gli autori

• Scuderi M. , Prete P. , Miccoli I. , Lovergine N. , Spinella C. , Nicotra G.

Titolo volume/Rivista

Non Disponibile

Anno di pubblicazione

2015

ISSN

Non Disponibile

ISBN

Non Disponibile

Numero di citazioni Wos

Nessuna citazione

Ultimo Aggiornamento Citazioni

Non Disponibile

Numero di citazioni Scopus

Non Disponibile

Ultimo Aggiornamento Citazioni

Non Disponibile

Settori ERC

Non Disponibile

Codici ASJC

Non Disponibile