Abstract

Stoichiometric CdSe nanotubes (NTs) with a length of ∼ 700 nm have been successfully grown by one-step electrochemical technique into Anodic Alumina Membranes. Ciclovoltammetric method has been performed using porous anodic alumina as template electrode and an electrochemical bath containing Cd2+ ions and SeO2. The as-prepared NTs have been identified as face-centred-cubic CdSe by XRD, while Micro-Raman analysis reveals the typical peaks of nanostructured CdSe. The stoichiometric deposition of CdSe NTs formation is suggested by EDX analysis, with an average atomic percentage of Cd:Se of ∼ 0.93. Photoelectrochemical measurements reveal that CdSe NTs are photoactive materials with direct band gap of 1.75 eV and n-type semiconducting behaviour.

Autore Pugliese

• Bocchetta Patrizia

Tutti gli autori

• Bocchetta P. , Santamaria M. , Di Quarto F.

Titolo volume/Rivista

ELECTROCHIMICA ACTA

Anno di pubblicazione

2013

ISSN

0013-4686

ISBN

Non Disponibile

Numero di citazioni Wos

Nessuna citazione

Ultimo Aggiornamento Citazioni

Non Disponibile

Numero di citazioni Scopus

Non Disponibile

Ultimo Aggiornamento Citazioni

Non Disponibile

Settori ERC

Non Disponibile

Codici ASJC

Non Disponibile