Abstract

In this study, H2Pc/Epoxy nanocomposite coating was fabricated for anti-corrosion applications. The electrochemical, cross-cut adhesion, impact resistance, bend test, contact angle, scanning electron microscopy (SEM) and thermogravimetric analysis (TGA) analysis were employed to evaluate the performance of new nanocomposites. Corrosion monitoring was achieved in saline solution (3.0 wt.% NaCl). The improvement of the corrosion performance of the epoxy coating containing H2Pc particles by comparison with neat epoxy resin was confirmed by the high coating resistance. Degradation of H2Pc/Epoxy nanocomposite coating was observed after 14 days. It was found that H2Pc particles improved the cross-cut adhesion, impact resistance and thermal stability of epoxy resin.

Autore Pugliese

• Mele Giuseppe Agostino , Bloise Ermelinda

Tutti gli autori

• Deyab M. A. , De Riccardis A. , Bloise E. , Mele G.

Titolo volume/Rivista

PROGRESS IN ORGANIC COATINGS

Anno di pubblicazione

2018

ISSN

0300-9440

ISBN

Non Disponibile

Numero di citazioni Wos

Nessuna citazione

Ultimo Aggiornamento Citazioni

Non Disponibile

Numero di citazioni Scopus

Non Disponibile

0

Ultimo Aggiornamento Citazioni

26/04/2018

Settori ERC

Non Disponibile

Codici ASJC

Non Disponibile