Abstract

The present study demonstrates an approach for fabricating fiber-reinforced ceramic matrix composites (CMCs) involving the coating of 2-dimensional woven alumina fibers with zirconia layer by sol gel, followed by impregnation of these coated fibers with alumina matrix and pressureless sintering. To emphasize the benefits of the zirconia coating on these CMCs, a reference sample without interfacial coating layer was prepared. The zirconia-coated CMCs showed superior flexural strength and thermal shock resistance compared with their uncoated counterparts. Foreign object damage tests carried out on the ZrO2 coated CMCs at high impact speed showed localized damage without any shattering.

Autore Pugliese

• Licciulli Antonio Alessandro

Tutti gli autori

• A. Licciulli , A. Chiechi , M. Fersini , K. P. Sanosh , A. Balakrishnan

Titolo volume/Rivista

INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY

Anno di pubblicazione

2012

ISSN

1546-542X

ISBN

Non Disponibile

Numero di citazioni Wos

Nessuna citazione

Ultimo Aggiornamento Citazioni

Non Disponibile

Numero di citazioni Scopus

Non Disponibile

Ultimo Aggiornamento Citazioni

Non Disponibile

Settori ERC

Non Disponibile

Codici ASJC

Non Disponibile