Abstract

Poly(ethylene glycol) diacrylate (PEGDA) cryogels, particularly useful for biotechnological applications, are currently fabricated exploiting crosslinking systems that require long freezing/crosslinking times (20 h or longer). The aim of this work was to assess whether fast UV irradiation (up to 60 s) of frozen PEGDA solutions could be an advantageous alternative for cryogel production. By using different polymer concentrations and UV times, cryogels with highly interconnected macropores (about 50–90 μm) were produced. A gelation yield in the range 60–80% was recorded, with higher values obtained for low PEGDA concentrations (5 and 10% w/v). Interestingly, while decreasing the swelling and increasing the stiffness of the cryogels, a higher polymer concentration was also found to reduce the pore size. Furthermore, increasing the UV time resulted in significantly higher swelling and larger pores for 10% PEGDA samples, while having negligible effect on other cryogel types and/or features. Although deserving further exploration, fast UV irradiation is an effective method to produce PEGDA cryogels with tunable properties.

Autore Pugliese

• Salvatore Luca , Sannino Alessandro , Madaghiele Marta , Demitri Christian

Tutti gli autori

• Madaghiele M. , Salvatore L. , Demitri C. , Sannino A.

Titolo volume/Rivista

MATERIALS LETTERS

Anno di pubblicazione

2018

ISSN

0167-577X

ISBN

Non Disponibile

Numero di citazioni Wos

Nessuna citazione

Ultimo Aggiornamento Citazioni

Non Disponibile

Numero di citazioni Scopus

Non Disponibile

0

Ultimo Aggiornamento Citazioni

26/04/2018

Settori ERC

Non Disponibile

Codici ASJC

Non Disponibile