Abstract

We demonstrate the fabrication of all-inorganic heterostructured n–p junction devices made of colloidal PbS quantum dots (QDs) and TiO2 nanorods (NRs). The entire device fabrication procedure relies on room-temperature processing, which is compatible with flexible plastic substrates and low-cost production. Through Kelvin Probe Force Microscopy and femtosecond pump and probe spectroscopy we decipher the electron transfer process occurring at the interface between the colloidal PbS QDs and TiO2 anatase NRs. Overall we demonstrate a high power conversion efficiency of [similar]3.6% on glass and [similar]1.8% on flexible substrates, which is among the highest reported for entirely inorganic-nanocrystal based solar cells on plastic supports.

Autore Pugliese

• Cozzoli Pantaleo Davide , Gigli Giuseppe

Tutti gli autori

• A. Loiudice , A. Rizzo , G. Grancini , M. Biasiucci , M. R. Belviso , M. Corricelli , M. L. Curri , M. Striccoli , A. Agostiano , P.D. Cozzoli , A. Petrozza , G. Lanzani , G. Gigli

Titolo volume/Rivista

ENERGY & ENVIRONMENTAL SCIENCE

Anno di pubblicazione

2013

ISSN

1754-5692

ISBN

Non Disponibile

Numero di citazioni Wos

26

Ultimo Aggiornamento Citazioni

28/04/2018

Numero di citazioni Scopus

Non Disponibile

Ultimo Aggiornamento Citazioni

Non Disponibile

Settori ERC

Non Disponibile

Codici ASJC

Non Disponibile