Abstract

Free-standing Chitosan/phosphotungstic acid polyelectrolyte membranes were prepared by an easy and fast in-situ ionotropic gelation process performed at room temperature. Scanning electron microscopy was employed to study their morphological features and their thickness as a function of the chitosan concentration. The membrane was tested as proton conductor in low temperature H2–O2 fuel cell allowing to get peak power densities up to 350 mW cm−2. Electrochemical impedance measurements allowed to estimate a polyelectrolyte conductivity of 18 mS cm−1.

Autore Pugliese

• Bocchetta Patrizia

Tutti gli autori

• Santamaria M. , Pecoraro C. M. , Di Quarto F. , Bocchetta P.

Titolo volume/Rivista

JOURNAL OF POWER SOURCES

Anno di pubblicazione

2015

ISSN

0378-7753

ISBN

Non Disponibile

Numero di citazioni Wos

Nessuna citazione

Ultimo Aggiornamento Citazioni

Non Disponibile

Numero di citazioni Scopus

12

Ultimo Aggiornamento Citazioni

22/04/2018

Settori ERC

Non Disponibile

Codici ASJC

Non Disponibile